| 高錳鋼陶瓷復合鄂破齒板 | | 來源： 點擊數：3166次 更新時間：2020-5-14 10:23:59 | | | | 詳細簡紹： | |
高錳鋼陶瓷復合鑄造圓錐破襯板（動/靜錐）及鄂破齒板
The High Manganese Steel matrix ceramic composite Mantle/Concave and Jaw plate
高錳鋼陶瓷復合鑄造圓錐破襯板（動/靜錐）及鄂破齒板，即在高錳鋼耐磨材料中熔鑄陶瓷顆粒，形成陶瓷金屬復合材料層，這層復合層的耐磨性能可達高鉻材料的2-3倍，同時繼承了高錳鋼的耐沖擊性能，
通常，基材選用= Mn18Cr2
熱處理后高錳鋼本體硬度= HB160-220 （沖擊后=HB500）
陶瓷顆粒硬度= HV1400
熱處理后陶瓷顆粒硬度=HRC60-70
熱處理后陶瓷顆粒間硬度= HB400-HB500
陶瓷復合材料扎臼壁的使用壽命是常規高錳鋼的2倍以上，其適用范圍比高鉻材料更廣泛。
The High Manganese Steel matrix ceramic composite Mantle/Concave and Jaw plate; That is ceramic particles are fused and cast in the wear-resistant material of High Manganese Steel to form ceramic metal composite layer. The wear-resisting property of the composite layer can reach 2-3 times that of the high chromium material, and it inherits the impact resistance of the High Manganese Steel.
Normally, the basis material = Mn18Cr2
Hardness of high manganesesteel after heat treatment （Impact hardness= HB500)
Hardness ceramic particles= HV1400
Hardness ceramic particles afterheat treatment=HRC60-70
Hardness between ceramic particles after heattreatment= HB400-HB500
The service life of the ceramic composite Mantle/Concave and Jaw plate is more than 2 times that of the High Manganese Steel. | | 【刷新頁面】【加入收藏】【打印此文】 【關閉窗口】 | | 上一篇：陶瓷復合軋臼壁 下一篇：陶瓷復合襯板/溜槽 |
|